Electrically Conductive Silicone Materials

Engineering Materials - Selection Guide
Controlled Volatility - Electrically Conductive Silicone

 

NuSil ID Cure System
Work Time
Mix Ratio
 Comments
CV-1500 Oxime 10 M 1 Part 2.1 ohm - cm Primed Lap Shear 300psi (2.1MPa)
CV-2640 PT Addition 2 HR 10:1 1.67 ohm - cm Carbon Fiber-filled Primed Lap Shear 250psi (1.7MPa)
CV-2644 PT Addition 2 HR 20:1 0.004 ohm - cm Young's Modulus 1400psi (9.7MPa)
CV-2646 Tin Condensation 2 HR 100:0.5 0.004 ohm - cm Young's Modulus 950psi (6.6MPa)
CV-2647 Tin Condensation 100:0.2 0.2 ohm -cm Primed Lap Shaer 115psi (0.8MPa)
CV1-2640 PT Addition 4 HR 10:1 30 ohm - cm Pumpable
CV2-2640 PT Addition 25 M 1:1 1:1 Mix Ratio Carbon Black-Filled 20 ohm - cm
CV2-2646 Tin Condensation 100:0.5 Remains Conductive at High Temperatures 0.001 ohm-cm(1.5W/mK)